Buxly Zinc Rich Epoxy Primer adheres perfectly to provide a continuous film of zinc metal to iron or steel surfaces and provides a matt finish which offers rust prevention on the surfaces.
Buxly Zinc Rich Epoxy Primer can be applied on the job to provide zinc cathodic protection, where usual methods of galvanizing are not applicable, such as transmission towers, television towers, machine installations, air conditioning ducts, metal roofs and refrigeration equipment etc.
| Type | Two Pack |
| Composition | Refined zinc dust pigment, inert extenders, special additives in epoxy resin cured with polyamide hardener |
| Mixing Ratio | Component A : 4 Parts by volume Component B : 1 Parts by volume |
| Pot Life of Mixed Paint | 3 to 4 Hours at 25° C |
| Application | Brush/Roller/Spray |
| Drying Time | a) Surface Dry : Within 1 Hour b) Tack Free : 6 – 8 Hours c) Hard Dry : 18-24 Hours d) Over-coating : Six days max |
| Complete Curing of Film | 96 Hours to obtain completely cured system |
| Theoretical Spreading Rate | 9–10 m2 per liter |
| Dry Film Thickness | 72 + 2 microns |
| No. of Coats | 1 Coat |
| Finish | Egg Shell to Matt |
| Volume Solids When Mixed | 50 + 2 % |
| Top Coat | Buxly’s High Build Epoxy Finishing EP-F-10 |
| Packing | 4 Liters pack size |
| Storage Stability | Six months, when stored properly in original sealed container at 15 to 35° C |